Hyundai EP PA6 LS405
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | HYUNDAI EP Co., Ltd. |
| Trademark: | Hyundai EP PA6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xTogOw_Hyundai-EP-PA6-LS405.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hyundai EP PA6 LS405 is a Polyamide 6 (Nylon 6) product. It is available in Asia Pacific. Typical application: Electrical/Electronic Applications. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ASTM D1505 |
| Molding Shrinkage - Flow | 1.2 to 1.7 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 83.4 | MPa | ASTM D638 |
| Flexural Modulus | 3040 | MPa | ASTM D790 |
| Flexural Strength | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 74 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 83.0 | °C | ASTM D648 |
| Melting Temperature | 220 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 to 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 3.5 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 30S5150 | The Matrixx Group, Inc. | PBT | Matrixx |
| POLYNIL® P270 | Nilit Plastics | Nylon 66 | POLYNIL® |
| Stylac™ 769 | Asahi Kasei Chemicals Corporation | AS | Stylac™ |
| Thermoset Plastics EP-22 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| Infino TP-1020 | SAMSUNG SDI CO., LTD. | PC | Infino |