Silamid® SV30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Roonamid a.s. |
| Trademark: | Silamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xTE9YS_Silamid-SV30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA6 reinforced with 30 % short glass fibres, natural and black colour and in colourly shades according to customer´s requests, optimal flowing properties, technical mouldings with increased claims to rigidity, strength, shape stability, eventually electroinsulating properties |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | 1.36 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ||||
| Across Flow | 1.3 | 1.3 | % | |
| Flow | 0.40 | 0.40 | % | |
| Water Absorption (23°C, 24 hr) | 0.90 | 0.90 | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9500 | 6200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 170 | 110 | MPa | ISO 527-2 |
| Flexural Modulus | 7200 | 5000 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 65 | 80 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | -- | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | -- | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | -- | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | -- | 4.70 | IEC 60250 | |
| Dissipation Factor (1 MHz) | -- | 0.12 | IEC 60250 | |
| Arc Resistance | 95.0 | -- | sec | ASTM D495 |
| Comparative Tracking Index (Solution A) | -- | 500 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 | |
| Glow Wire Ignition Temperature | 650 | 650 | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRF3803 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| BESTNYL SI00VI02BEHX | Triesa Plastics | Nylon 6 | BESTNYL |
| KumhoSunny PBT/ABS HBG5710 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS+PBT | KumhoSunny PBT/ABS |
| LEXAN™ HPH4404 resin | SABIC Innovative Plastics | PC+PPC | LEXAN™ |
| Sylvin 8215-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |