LNP™ LUBRILOY™ DF204 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xStQNb_LNP-LUBRILOY-DF204-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY DF204 is a compound based on Polycarbonate resin containing 20% Glass Fiber, Proprietary Lubricant. Added feature of th is grade is: Wear Resistant. Also known as: LNP* LUBRILOY* Compound DF-20 Product reorder name: DF204 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.30 | % | |
| Across Flow : 24 hr | 0.20 to 0.30 | % | |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 6760 | MPa | ASTM D638 |
| Tensile Strength (Break) | 105 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.8 | % | ASTM D638 |
| Flexural Modulus | 6000 | MPa | ASTM D790 |
| Flexural Strength | 159 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.41 | ||
| vs. Itself - Static | 0.39 | ||
| Wear Factor - Washer | 179 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 180 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 760 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 142 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 138 | °C | |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 7.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.8E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.25 | W/m/K | ASTM E1530 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 299 to 310 | °C | |
| Front Temperature | 304 to 316 | °C | |
| Processing (Melt) Temp | 304 to 316 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBB2672 | Teknor Apex Asia Pacific PTE. LTD. | LDPE | Sinpolene |
| Adell PP EP-18 | Adell Plastics, Inc. | PP, Unspecified | Adell PP |
| King Pearl® G-XL | Loyal Chemical | PS (EPS) | King Pearl® |
| Karina YELLOW PVC COMPOUND 804-02/ 69-Y-RTC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9067F3 Red 6252 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |