ULTEM™ AR9200 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xSpHGG_ULTEMAR9200resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 5.7 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 - 0.50 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 6960 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 152 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 7240 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 100 mm Span) | 207 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Reverse Notch Izod Impact (3.20 mm) | 530 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 211 | °C | ASTM D648 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| FAA Flammability 6 | NATURAL | FAR 25.853 | |
| NBS Smoke Density | ASTM E662 | ||
| Flaming, Dmax | 5.00 | ASTM E662 | |
| Flaming, Ds, 1.5 min | 0.00 | ASTM E662 | |
| Flaming, Ds, 4 min | 5.00 | ASTM E662 | |
| OSU peak heat release rate 7 | 40.0 | kW/m² | FAR 25.853 |
| OSU total heat release 8 | 5.00 | kW·min/m² | FAR 25.853 |
| Vertical Burn Test | FAR 25.853 | ||
| Test a (60 s), passes at | 0.0 | hr | FAR 25.853 |
| Test b (12 s), passes at | 0.0 | hr | FAR 25.853 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 343 - 366 | °C | |
| Middle Temperature | 354 - 377 | °C | |
| Front Temperature | 366 - 388 | °C | |
| Nozzle Temperature | 360 - 382 | °C | |
| Processing (Melt) Temp | 366 - 388 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | Method A/B |
| 7 . | 5 minute test |
| 8 . | 2 minute test |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 TFE 15 LP | RTP Company | Acetal (POM) Copolymer | RTP |
| Salflex 830I | Salflex Polymers Ltd. | PP, Unspecified | Salflex |
| Utomer UT860D | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyester | Utomer |
| Kynar® 8600 | Arkema | Plastics Additive, Other | Kynar® |
| ICORENE® N7020 | ICO Polymers EMEA, A Division of A. Schulman | LDPE | ICORENE® |