VECTRA® E135i
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xQi65k_VECTRA-E135i.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
35% glass fiber filled /Higher weldline strength. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant. FDA compliant. UL-Listing V-0 in all colors at .15mm thickness per UL 94 flame testing. UL = Underwriters Laboratories (USA) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.67 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.29 | % | ISO 294-4 |
| Flow direction | 0.0 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.070 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 62 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 16000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 150 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 17000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 225 | MPa | ISO 178 |
| Compressive Modulus | 13500 | MPa | ISO 604 |
| Compressive Stress (1% Strain) | 100 | MPa | ISO 604 |
| Flexural Strain at Break | 2.1 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 27 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 30 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 275 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | °C | ISO 306/B50 |
| Melting Temperature 1 | 335 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 5.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral | 5.9E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity | |||
| 1 MHz | 4.10 | IEC 60250 | |
| 2.05 GHz | 4.37 | Internal method | |
| Dissipation Factor | |||
| 1 MHz | 3.0E-3 | IEC 60250 | |
| 2.05 GHz | 6.0E-3 | Internal method | |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 315 - 335 | °C | |
| Middle Temperature | 320 - 345 | °C | |
| Front Temperature | 325 - 355 | °C | |
| Nozzle Temperature | 335 - 350 | °C | |
| Processing (Melt) Temp | 335 - 355 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 150 | MPa |
| Injection instructions |
|---|
| Zone 4 Temperature: 330 to 360°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1005 FR A HI | RTP Company | PBT | RTP |
| Moplen RP344R | PolyMirae | PP Random Copolymer | Moplen |
| Triapol® Blends C3 K46 PRTA011 BS310 MSP | Petropol Industry and Trade of Polymers LTDA | PC+ABS | Triapol® Blends |
| 3M™ Dyneon™ Fluoroplastic PFA 6503PAZ | 3M Advanced Materials Division | PFA | 3M™ Dyneon™ Fluoroplastic |
| HOPELEN FR-160 | Lotte Chemical Corporation | PP Homopolymer | HOPELEN |