Next Nylon 66 Prime Series PXR-01BK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 66 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xQSW29_Next-Nylon-66-Prime-Series-PXR-01BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA66 Un Filled Black Compound Product Applications Cable tie, Fasteners and connectors Benefits Excellent filling quality Good thermal resistance, high strength & V2 Rating under 0.4mm. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.14 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 1.2 | -- | % | ASTM D955 |
| Transverse flow | 1.2 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 1.2 | -- | % | ASTM D570 |
| Saturation 1 | 8.5 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3100 | 1800 | MPa | ASTM D638 |
| Tensile Strength | 85.0 | 55.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | > 50 | % | ASTM D638 |
| Flexural Modulus | 2900 | -- | MPa | ASTM D790 |
| Flexural Strength | 120 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 49 | 78 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | No Break | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 200 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 75.0 | -- | °C | ASTM D648 |
| Melting Temperature | 262 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 27 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 850 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.800 mm) | 725 | -- | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 干燥 This grade is not suitable for food contact, medical devices or toy applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 270 - 280 | °C | |
| Front Temperature | 280 - 290 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TP SD 300 90A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| Vydyne® 47H BK11 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| HiFill® POM CO 0374 S | Techmer Engineered Solutions | Acetal (POM) Copolymer | HiFill® |
| KEBAFORM® C 90 M | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| Sumikon® PM-9820 | SBHPP | Phenolic | Sumikon® |