BMC 2201
| Category: | Alkyd , Alkyd |
| Manufacturer: | Bulk Molding Compounds, Inc. |
| Trademark: | BMC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xQR6Xm_BMC-2201.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BMC 2201 molding compound is a mineral filled, glass-fiber-and nylon-floc reinforced alkyd compound suitable for compression and transfer molding. It was developed for applications requiring better abrasion resistance than that available with other BMC products. BMC 2201 molding compound is produced in extruded form in a range of industrial colors. It is available in logs up to 12 inches in length or as precut slugs, of specific weight, in diameters from ¾ " to 2 7/8 ". Within this range smaller diameters are supplied as multiple extrusions and weight tolerances are plus or minus 5% up to a maximum of of plus 15 grams. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.09 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 65 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strength | 121 | MPa | ASTM D790 |
| Compressive Strength | 176 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 232 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | 12 | kV/mm | ASTM D149 |
| Dielectric Constant (60 Hz) | 7.30 | ASTM D150 | |
| Dissipation Factor (60 Hz) | 0.040 | ASTM D150 | |
| Arc Resistance | 130 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 500 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | HB | ||
| 3.18 mm | HB | ||
| 6.35 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 138 to 166 | °C |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRF6603 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| SOLPLAST TH 9000C | UTEKSOL d.o.o. | SBS | SOLPLAST TH |
| GAPEX® RPP43EV01NA | Ferro Corporation | PP Homopolymer | GAPEX® |
| GXL 10009NH | S&E Specialty Polymers, LLC | TPO (POE) | GXL |
| ESENTTIA 35R80 | Polipropileno del Caribe S.A. | PP Random Copolymer | ESENTTIA |