LNP™ LUBRICOMP™ RFL369 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xPxbrK_LNP-LUBRICOMP-RFL369-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RFL369 is a compound based on PA 66 resin containing Glass Fiber, PTFE, Flame Retardant. Added features include: Flame Retardant, internally lubricated Also known as: LNP* LUBRICOMP* Compound RFL-4036 FR Product reorder name: RFL369 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.74 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 128 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.7 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 8500 | MPa | ISO 178 |
| Flexural Stress | 152 | MPa | ISO 178 |
| Flexural Strain at Break 2 | 2.5 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 253 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 225 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 4.2E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 7.8E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXT REGRIND POMH 500P-300RG | NEXT Specialty Resins, Inc. | Acetal (POM) Homopolymer | NEXT REGRIND |
| Nypol® PA A3 G30 BRC0001 NR392 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| APEX® 3080-H | Teknor Apex Company | PVC, Flexible | APEX® |
| FRIANYL® B3 GF25 V0 | Nilit Plastics | Nylon 6 | FRIANYL® |
| HIVAL® 2620 | Nexeo Solutions, LLC. | PP Impact Copolymer | HIVAL® |