Badamid® A70 CF20 HHC
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xPiyDH_Badamid-A70-CF20-HHC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Heat stabilized Polyamide 6.6 injection moulding grade, 20% carbon fibres reinforcement for technical products with good electrical properties |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.22 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.8 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.2 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 1(23°C) | 16500 | 11500 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Break, 23°C) | 225 | 155 | MPa | ISO 527-2/5 |
| Tensile Strain 3(Break, 23°C) | 2.5 | 5.5 | % | ISO 527-2/5 |
| Flexural Stress 4(23°C) | 315 | 245 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 5 | ISO 179/1eA | |||
| -30°C | 8.0 | -- | kJ/m² | |
| 23°C | 10 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength 6 | ISO 179/1eU | |||
| -30°C | 50 | -- | kJ/m² | |
| 23°C | 60 | 75 | kJ/m² | |
| Notched Izod Impact Strength 7(23°C) | 12 | 20 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 8 | ||||
| 0.45 MPa, Unannealed | 245 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 9 | 262 | -- | °C | ISO 3146 |
| Maximum Service Temperature | IEC 216 | |||
| 20000 hrs | 130 | -- | °C | |
| some hours | 240 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 10 | 1.0E+3 | -- | ohms | IEC 60093 |
| Comparative Tracking Index | 100 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm 11 | HB | -- | ||
| 1.60 mm 12 | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | 80x10x4 mm |
| 5 . | 80x10x4 mm |
| 6 . | 80x10x4 mm |
| 7 . | 80x10x4 mm |
| 8 . | 110x10x4 mm |
| 9 . | 10 K/min, Compound for moulding |
| 10 . | 80x80x1 mm |
| 11 . | 125x13x0.8 mm |
| 12 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRAMID® 4210G15 | Samyang Corporation | Nylon, Unspecified | TRAMID® |
| Bergamid™ A70 G30 MOS2 NC721 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Fainplast PVC GK 80 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Tenac™ 2013A | Asahi Kasei Corporation | Acetal (POM) Homopolymer | Tenac™ |
| CYCOLAC™ FXS610SK resin | SABIC Innovative Plastics Europe | ABS | CYCOLAC™ |