ExxonMobil™ PP7011L1
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | ExxonMobil™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xPaCvX_ExxonMobil-PP7011L1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| An impact-resistant copolymer resin suitable for extrusion applications, which has high melt viscosity and excellent low-temperature impact strength. It is suitable for cables, pipes, profiles, sheets and thermoforming. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 1.2 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 4.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 1270 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 26.9 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2/50 |
| Flexural Modulus - Secant | 1240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C, complete fracture | 3.8 | kJ/m² | ISO 179 |
| 0°C, complete fracture | 5.4 | kJ/m² | ISO 179 |
| 23°C, local fracture | 29 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C, Partial Break) | 32 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 79.6 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 50.2 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 152 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 161 | °C | ISO 3146 |
| Peak Crystallization Temperature (DSC) | 112 | °C | ISO 3146 |
| Legal statement |
|---|
| 本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitalac® 8540S | Taita Chemical Company, Ltd. | ABS | Taitalac® |
| Nymax™ GF 1200 A 40 IM Black 13A | PolyOne Corporation | Nylon 66 | Nymax™ |
| Desmopan® 1350D | Covestro - PUR | TPU-Polyester | Desmopan® |
| Kotex KG-30MRA | Kotec Corporation | PC | Kotex |
| Sylvin 9925-85 BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |