PRL PPX/NY-G30
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xOdbtP_PRL-PPX-NY-G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PRL PPX/NY-G30 is a Polyphenylene Ether + PS + Nylon (PPE+PS+Nylon) product filled with 30% glass fiber. It can be processed by injection molding and is available in North America. Primary characteristic: rohs compliant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/3.8 kg) | 1.0 to 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18 mm | 0.20 to 0.40 | % | |
| Across Flow : 3.18 mm | 0.50 to 0.90 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 148 | MPa | |
| Break, 3.18 mm | 148 | MPa | |
| Tensile Elongation (Break, 3.18 mm) | 6.0 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 8140 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 221 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.18 mm | 53 | J/m | |
| 23°C, 3.18 mm | 80 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 232 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 227 | °C | |
| Vicat Softening Temperature | 229 | °C | ASTM D1525 1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 to 107 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 266 to 304 | °C | |
| Middle Temperature | 271 to 304 | °C | |
| Front Temperature | 277 to 316 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 79.4 to 121 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1160 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Dynacom CR-120 | Dynachem Co. Ltd. | PP Copolymer | Dynacom |
| HiFill FR® ABS FR | Techmer Engineered Solutions | ABS | HiFill FR® |
| LubriOne™ PC-20GF/15T NC042 S-RoHs | PolyOne Corporation | PC | LubriOne™ |
| Plaslube® PA6/6 GF40 ML5 HS BK | Techmer Engineered Solutions | Nylon 66 | Plaslube® |