SABIC® HDPE ICP5008
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xOHwP2_SABIC-HDPE-ICP5008.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE ICP5008 is part of SABIC's high density polyethylene Industrial Container Product portfolio. SABIC® HDPE ICP5008 combines good mechanical/processing properties with good ESCR performance. The material is supplied as natural pellets without UV package. The material can be coloured with a master batch. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.949 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 7.0 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (10% Igepal CO-630, Compression Molded, F50) | 800 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 950 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 23.0 | MPa | |
| Break, 2.00 mm, Compression Molded | 34.0 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 1000 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1000 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 24.0 | MPa | ISO 178 |
| ESCR (Strain Hardening) - Gp | 30.0 | MPa | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Enthalpy Change | 192 | J/g | DIN 53765 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (-30°C, Compression Molded) | 15 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 77.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 126 | °C | ISO 306/A |
| Melting Temperature (DSC) | 131 | °C | DIN 53765 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPC 12712 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Akulon® K224-PG6 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Flexalloy® 9600-72 | Teknor Apex Company | PVC Elastomer | Flexalloy® |
| LEXAN™ DMX2415 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Sylvin 8925-70UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |