LNP™ THERMOCOMP™ 9X07435X compound
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xOE8Nr_LNP-THERMOCOMP-9X07435X-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP 9X07435X is a compound based on Miscellaneous resin containing Proprietary Filler(s). Added fature of this grade is: Plateable. Also known as: LNP* THERMOCOMP* Compound 9X07435X Product reorder name: 9X07435X |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.90 to 1.1 | % | |
| Across Flow : 24 hr | 1.1 to 1.3 | % | |
| Water Absorption (24 hr, 50% RH) | 0.098 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5460 | MPa | ASTM D638 |
| -- | 4820 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 60.1 | MPa | ASTM D638 |
| Yield | 51.2 | MPa | ISO 527-2/5 |
| Break 3 | 59.9 | MPa | ASTM D638 |
| Break | 51.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.9 | % | ASTM D638 |
| Yield | 1.6 | % | ISO 527-2/5 |
| Break 5 | 1.9 | % | ASTM D638 |
| Break | 1.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 5350 | MPa | ASTM D790 |
| -- 7 | 5010 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 93.5 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 95.3 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 95.8 | MPa | ASTM D790 |
| Flexural Strain at Break 10 | 2.2 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 35 | J/m | ASTM D256 |
| 23°C 11 | 3.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 270 | J/m | ASTM D4812 |
| 23°C 12 | 19 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 101 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 111 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1.00 GHz) | 2.90 | ASTM D150 | |
| Dissipation Factor (1.00 GHz) | 4.7E-3 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 299 to 310 | °C | |
| Middle Temperature | 299 to 310 | °C | |
| Front Temperature | 299 to 310 | °C | |
| Nozzle Temperature | 299 to 310 | °C | |
| Processing (Melt) Temp | 299 to 310 | °C | |
| Mold Temperature | 107 to 121 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 2 mm/min |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vipel® K190-BPT-15 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| Fainplast PVC ARC 20 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Epocast 1635 A/B | Huntsman Advanced Materials | Epoxy | Epocast |
| KW Plastics KW 308A | KW Plastics | PP Impact Copolymer | KW Plastics |
| Karina CLEAR PVC COMPOUND -E 84/203-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |