Sarlink® TPV X17165B
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xNsVD3_Sarlink-TPV-X17165B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The Sarlink 17100 Series are super high flow injection molding grades with excellent UV resistance for exterior applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, 5 sec, Extruded | 65 | ||
| Shore A, 5 sec, Injection Molded | 67 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| Across Flow : 100% Strain | 2.10 | MPa | |
| Flow : 100% Strain | 2.40 | MPa | |
| Tensile Strength | ISO 37 | ||
| Across Flow : Break | 4.20 | MPa | |
| Flow : Break | 4.10 | MPa | |
| Tensile Elongation | ISO 37 | ||
| Across Flow : Break | 450 | % | |
| Flow : Break | 380 | % | |
| Tear Strength - Across Flow 1 | 20 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 22 hr | 20 | % | |
| 70°C, 22 hr | 32 | % | |
| 125°C, 70 hr | 44 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | ISO 188 | ||
| 135°C, 1000 hr | -10 | % | |
| 150°C, 168 hr | -15 | % | |
| Change in Tensile Modulus in Air - Across Flow | ISO 188 | ||
| 135°C, 1000 hr | 5.0 | % | |
| 150°C, 168 hr | 0.0 | % | |
| Change in Ultimate Elongation in Air - Across Flow | ISO 188 | ||
| 135°C, 1000 hr | -18 | % | |
| 150°C, 168 hr | -20 | % | |
| Change in Shore Hardness in Air | ISO 188 | ||
| 135°C, 1000 hr | 2.0 | ||
| 150°C, 168 hr | 0.0 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary, 206 1/s (200°C) | 200 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 to 205 | °C | |
| Middle Temperature | 180 to 205 | °C | |
| Front Temperature | 180 to 205 | °C | |
| Nozzle Temperature | 185 to 210 | °C | |
| Processing (Melt) Temp | 185 to 210 | °C | |
| Mold Temperature | 10.0 to 55.0 | °C | |
| Back Pressure | 0.100 to 1.00 | MPa | |
| Screw Speed | 100 to 200 | rpm |
| Note Message | |
|---|---|
| 1 . | Method Ba, Angle (Unnicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PH 49 GF 10 GB 20 | Plastcom | PP, Unspecified | SLOVALEN® |
| Tarflen® SM1 | Grupa Azoty S.A. | PTFE | Tarflen® |
| Ultralloy™ 3310-28 | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| LUVOCOM® 1/CF/15/HS | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| SQUARE® LIM3900-20A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |