CALIBRE™ 2061 HD 15
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xNndrT_CALIBRE-2061-HD-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 2061 HD 15 Polycarbonate Resins are designed for steam and ethylene oxide sterilization required by the health care industry. CALIBRE™ 2061 HD 15 Polycarbonate Resins offer a level of cleanliness/clarity and melt flow consistency that is superior for those applications with critical optical performance requirements. CALIBRE™ 2061 HD 15 Polycarbonate Resin has been tested under ISO 10993 standards This product contains mold release. Main Characteristics
Applications
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955, ISO 294-4 |
| Water Absorption | ASTM D570, ISO 62 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2300 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 62.1 | MPa | ASTM D638 |
| Yield | 62.0 | MPa | ISO 527-2/50 |
| Break 3 | 68.3 | MPa | ASTM D638 |
| Break | 68.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 5 | 150 | % | ASTM D638 |
| Break | 150 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 6 | 2400 | MPa | ASTM D790 |
| -- | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 96.5 | MPa | ASTM D790 |
| -- | 96.5 | MPa | ISO 178 |
| Taber Abrasion Resistance | 45 | % | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 25 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 1900 | J/m | ASTM D256 |
| 23°C | 74 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256, ISO 180 | |
| Instrumented Dart Impact 8(23°C, Total Energy) | 81.3 | J | ASTM D3763 |
| Tensile Impact Strength | 378 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed | 139 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 120 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa, Annealed | 136 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 148 | °C | ASTM D1525 9 |
| -- | 143 | °C | ISO 306/B50 |
| CLTE - Flow (-40 to 82°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149, IEC 60243-1 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.00 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 1.0E-3 | ||
| 1 MHz | 2.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 10(1.60 mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542, ISO 489 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 0.60 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 50 mm/min |
| 6 . | Method I (3 point load), 2.0 mm/min |
| 7 . | Method I (3 point load), 2.0 mm/min |
| 8 . | 3.39 m/sec |
| 9 . | Rate A (50°C/h), Loading 2 (50 N) |
| 10 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V936 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Radilon® S RV250 100 NAT | Radici Plastics | Nylon 6 | Radilon® |
| Bergamid™ NN-50GF/1M BK046 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Lupoy® 3030-15 | LG Chem Ltd. | PC | Lupoy® |
| MAJORIS BG164 | AD majoris | PP, Unspecified | MAJORIS |