| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | Eltex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xNWpkv_Eltex-PF6612AA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eltex® PF6612AA is a metallocene LLDPE grade produced in Europe. Benefits & Features Eltex® PF6612AA is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties:
Applications Eltex® PF6612AA has been developed for use in collation shrinkwrap, food packaging and other thin film applications where an excellent balance between film strength and rigidity is required together with good optical properties. In addition, Eltex® PF6612AA offers easy extrudability. If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.926 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.3 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 25 µm | 230 | MPa | |
| 1% Secant, TD : 25 µm | 270 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm | 13.0 | MPa | |
| TD : Yield, 25 µm | 13.0 | MPa | |
| MD : Break, 25 µm | 55.0 | MPa | |
| TD : Break, 25 µm | 50.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm | 570 | % | |
| TD : Break, 25 µm | 690 | % | |
| Dart Drop Impact (25 µm) | 200 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 160 | g | |
| TD : 25 µm | 560 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature 1 | 120 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm) | 65 | ASTM D2457 | |
| Haze (25.0 µm) | 7.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | 2nd heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® 700 314 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| WACKER SilGel® 612 A/B | Wacker Chemie AG | Silicone | WACKER SilGel® |
| CGPC PVC R-10X NI Bottle Blowing | China General Plastics Corporation | PVC, Flexible | CGPC PVC |
| Karina BLACK PVC COMPOUND 951-48/4-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9067-90 Grey 991 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |