DOWLEX™ 2027G
| Category: | LMDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xMlXnY_DOWLEX-2027G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.941 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film strength | ASTM D882 | ||
| MD : 25 µm | 113 | J/cm³ | ASTM D882 |
| TD : 25 µm | 124 | J/cm³ | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 16.2 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 10.8 | MPa | ASTM D882 |
| MD : Break, 25 µm | 39.0 | MPa | ASTM D882 |
| TD : Break, 25 µm | 28.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 580 | % | ASTM D882 |
| TD : Break, 25 µm | 740 | % | ASTM D882 |
| Dart Drop Impact (25 µm) | 43 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 34 | g | ASTM D1922 |
| TD : 25 µm | 210 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 123 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 127 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm) | 86 | ASTM D2457 | |
| Haze (25.4 µm) | 4.1 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 276 | °C |
| Extrusion instructions |
|---|
| 铸造薄膜的制造条件： 螺杆尺寸：3.5 英寸 (89 mm)；32:1 L/D 熔体温度：529°F (276°C) 螺杆尺寸：2.5 英寸 (63.5 mm)；24:1 L/D 熔体温度：515°F (268°C) 冷却辊温度：70°F (21°C) 生产线速度：500 fpm (152 米/分） |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® 1015CR BRIGHT | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |
| VENELENE® 11PG4 | Poliolefinas Internacionales, C.A. (Polinter) | LLDPE | VENELENE® |
| apilon 52® D1 45L | API SpA | TPU-Polyester | apilon 52® |
| INSULCAST® 333/INSULCURE 9 | ITW Polymers Coatings North America | Epoxy | INSULCAST® |
| Lion Idemitsu Composites PPS G131L3 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |