SCHULAMID® 66 MV HI H K1416
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xMEzyH_SCHULAMID-66-MV-HI-H-K1416.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Impact modified and heatstabilized polyamide 66 grade |
| General Information | |
|---|---|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.08 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (Saturation, 23°C) | 2.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2100 | 750 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 55.0 | 40.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 5.5 | 25 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | > 40 | > 100 | % | ISO 527-2/1A/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 18 | -- | kJ/m² | |
| 23°C | 70 kJ/m² | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Vicat Softening Temperature | ||||
| -- | > 250 | -- | °C | ISO 306/A50 |
| -- | 210 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 30 | -- | mm/min | ISO 3795 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2000 A-670 | RTP Company | PSU+ABS | RTP |
| RTP 602 | RTP Company | ABS | RTP |
| Sinpolene MBB3401 | Teknor Apex Asia Pacific PTE. LTD. | LLDPE | Sinpolene |
| ACCUTECH™ CP0436G20CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| InnoFR™ FX-8091 | Innovative Polymers, Inc. | TSU | InnoFR™ |