Infino NH-1015S
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xLYIAt_InfinoNH1015S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Infino NH-1015S is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Infino NH-1015S applications include electrical/electronic applications and electrical appliances. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 36 | g/10 min | ASTM D1238 |
| 250°C/10.0 kg | 36 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 121 | ASTM D785 | |
| R scale | 121 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2400 | MPa | ASTM D638 |
| -- | 2500 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 59.0 | MPa | ASTM D638 |
| Yield | 61.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 47.0 | MPa | ASTM D638 |
| Fracture | 48.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 26 | % | ASTM D638 |
| Fracture | 27 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2400 | MPa | ASTM D790 |
| -- 6 | 2550 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 85.0 | MPa | ASTM D790 |
| -- 8 | 89.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 27 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 510 | J/m | ASTM D256 |
| 23°C 10 | 35 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 96.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 92.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 84.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 100 | °C | ISO 306/B50 |
| -- | 103 | °C | ISO 306/B120 |
| RTI Elec (1.5 mm) | 90.0 | °C | UL 746 |
| RTI Imp (1.5 mm) | 85.0 | °C | UL 746 |
| RTI (1.5 mm) | 90.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.5 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80 | °C | |
| Hot air dryer | 80 | °C | |
| Drying Time | |||
| -- | 3.0 | hr | |
| Hot air dryer | 2.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 250 - 270 | °C | |
| Front Temperature | 270 - 280 | °C | |
| Nozzle Temperature | 280 | °C | |
| Mold Temperature | 50 - 90 | °C | |
| Injection Pressure | 98.0 | MPa | |
| Back Pressure | 0.500 | MPa | |
| Screw Speed | 50 | rpm |
| Injection instructions |
|---|
| Hot Runner Manifold Temperature: 280°CHot Runner Valve Nozzle Temperature: 280°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon G1030H-01 | RheTech, Inc. | Nylon 6 | Rhelon |
| Sinpolene MBB2507 | Teknor Apex Asia Pacific PTE. LTD. | Nylon, Unspecified | Sinpolene |
| Borealis PE FT3200 | Borealis AG | LDPE | Borealis PE |
| KumhoSunny PET HEG3620NH | Shanghai KumhoSunny Plastics Co., Ltd. | PET | KumhoSunny PET |
| POBUX 3001EPG30 | POLYROCKS CHEMICAL CO., LTD | PBT | POBUX |