LG ABS HF390
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xLOaBs_LGABSHF390.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Description
Application
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 - 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 64 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 43.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 10 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2550 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 68.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 240 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 86.0 | °C | ASTM D648 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | HB | UL 94 | |
| 3.0 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70 - 80 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 180 - 200 | °C | |
| Middle Temperature | 190 - 210 | °C | |
| Front Temperature | 200 - 220 | °C | |
| Nozzle Temperature | 200 - 230 | °C | |
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 40 - 70 | °C | |
| Back Pressure | 0.490 - 1.47 | MPa | |
| Screw Speed | 30 - 50 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.01% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V899 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| MIDILENA III HDPE2200J | ROMPETROL PETROCHEMICALS S.R.L. | HDPE | MIDILENA III |
| DIALAC® KD102S | UMG ABS, Ltd. | AES | DIALAC® |
| Ecotan B FL HI 1 SB NAT | Soredi S.p.a. | Nylon 6 | Ecotan B |
| TECACOMP® PP HTE black 4099 | Ensinger GmbH | PP, Unspecified | TECACOMP® |