Hostacom SD068-4C
| Category: | PP, HMS , High Melt Strength Polypropylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xL6ILQ_Hostacom-SD068-4C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostacom SD068-4C fractional melt flow, 2,000 MPa flexural modulus, 40% calcium filled polypropylene copolymer is designed for blow molding and extrusion. This material is characterized by very good melt strength, excellent processability and an excellent impact/stiffness balance. Typical applications include wiring channels, ductwork and seat backs. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.40 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 23.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 300 | % | ISO 527-2 |
| Flexural Modulus | 2000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 55 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 97.0 | °C | ISO 75-2/B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® PSH 6093 | Marco Polo International, Inc. | PS (HIPS) | MARPOL® PSH |
| Matrixx 14N4003 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| Borealis PE FA6224 | Borealis AG | LDPE | Borealis PE |
| LNP™ LUBRICOMP™ DL0049EF compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| Sylvin 6428-90 Black | Sylvin Technologies Incorporated | CPE | Sylvin |