VALOX™ ENH4565 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xKWM2w_VALOXENH4565resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 33% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin, Good thermal shock resistance and low CTE. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.60 | g/cm³ | ASTM D792 |
| -- | 1.61 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 24 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/5.0 kg | 18.0 | cm³/10min | ISO 1133 |
| 265°C/5.0 kg | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow 1 | 0.10 - 0.40 | % | Internal method |
| Flow : 3.20mm | 0.10 - 0.40 | % | Internal method |
| Transverse flow 2 | 0.40 - 0.80 | % | Internal method |
| Transverse flow : 3.20mm | 0.40 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.23 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 3 | 11600 | MPa | ASTM D638 |
| -- | 11500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 4 | 137 | MPa | ASTM D638 |
| Yield | 140 | MPa | ISO 527-2/5 |
| Fracture 5 | 137 | MPa | ASTM D638 |
| Fracture | 140 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 6 | 2.4 | % | ASTM D638 |
| Yield | 2.4 | % | ISO 527-2/5 |
| Fracture 7 | 2.4 | % | ASTM D638 |
| Fracture | 2.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 8 | 9400 | MPa | ASTM D790 |
| -- 9 | 9400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 185 | MPa | ISO 178 |
| Yield, 50.0mm span 10 | 180 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -30°C | 12 | kJ/m² | ISO 179/2C |
| 23°C | 12 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength | ISO 179/2U | ||
| -30°C | 60 | kJ/m² | ISO 179/2U |
| 23°C | 60 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| -30°C | 60 | J/m | ASTM D256 |
| 23°C | 80 | J/m | ASTM D256 |
| -30°C 11 | 14 | kJ/m² | ISO 180/1A |
| 23°C 12 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | ASTM D4812 | ||
| -30°C | 600 | J/m | ASTM D4812 |
| 23°C | 800 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 9.40 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 218 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 206 | °C | ASTM D648 |
| Vicat Softening Temperature | 205 | °C | ASTM D1525 13 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 1.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flow : -40 to 150°C | 2.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 1.9E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 150°C | 9.8E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 80°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 140 | °C | UL 746 |
| RTI | 140 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 - 60.0 | °C | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Nozzle Temperature | 230 - 255 | °C | |
| Processing (Melt) Temp | 245 - 260 | °C | |
| Mold Temperature | 40.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Tensile Bar |
| 3 . | 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | Type 1, 5.0 mm/min |
| 7 . | Type 1, 5.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2800 B-65A | RTP Company | TPV | RTP |
| ColorRx® PEEK-3000RX | LTL Color Compounders, Inc. | PEEK | ColorRx® |
| DiaAlloy TA-35 | Mitsubishi Rayon America Inc. | PC | DiaAlloy |
| HONES® PBT GF30E | Guangdong Shunde Hones Polymer Material Co., Ltd. | PBT | HONES® |
| LUVOCOM® 80-7489 VP | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |