LNP™ THERMOCOMP™ RX00713H compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xIT4Yw_LNP-THERMOCOMP-RX00713H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RX00713H is a compound based on Nylon 6/6 containing proprietary fillers. Characteristics of this grade are: Healthcare. Also known as: LNP* THERMOCOMP* Compound PDX-R-00713 EES Product reorder name: RX00713H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.50 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.55 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.81 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13000 | MPa | ASTM D638 |
| -- | 13000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 200 | MPa | ASTM D638 |
| Break | 202 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 3.1 | % | ASTM D638 |
| Break | 2.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 11700 | MPa | ASTM D790 |
| -- 5 | 11300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 304 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 309 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C 7 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1200 | J/m | ASTM D4812 |
| 23°C 8 | 76 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 9.40 | J | ASTM D3763 |
| -- | 3.10 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 264 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 260 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 255 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 250 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.5E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.4E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3481-1 | RTP Company | LCP | RTP |
| Medalist® MD-12350 | Teknor Apex Company | TPE | Medalist® |
| Unichem 9011-Rad | Colorite Polymers | PVC, Unspecified | Unichem |
| Karina ADDITIVE CONCENTRATE MICRO EX-G (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Osterlene® LLB0918A | Osterman & Company | LLDPE | Osterlene® |