LNP™ LUBRICOMP™ RFL34 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xHY8wO_LNPLUBRICOMPRFL34compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RFL34 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound RFL-4034 Product reorder name: RFL34 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 1.3 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.9 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.9 | % | ISO 294-4 |
| Flow direction : 24 hours | 1.3 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.50 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8270 | MPa | ASTM D638 |
| -- | 8060 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 158 | MPa | ASTM D638 |
| Yield | 155 | MPa | ISO 527-2 |
| Fracture | 158 | MPa | ASTM D638 |
| Fracture | 155 | MPa | ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 3.3 | % | ASTM D638, ISO 527-2 |
| Fracture | 3.3 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 6890 | MPa | ASTM D790 |
| -- | 7000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 221 | MPa | ASTM D790 |
| -- | 223 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.60 | ASTM D3702 Modified | |
| With Self-Static | 0.60 | ASTM D3702 Modified | |
| Wear Factor - Washer | 10.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C 2 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1200 | J/m | ASTM D4812 |
| 23°C 3 | 68 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 10.2 | J | ASTM D3763 |
| -- | 4.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 262 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 262 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 253 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 250 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 7.2E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 3.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS 330 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Techsil TSP100 | Techsil Limited | Silicone | Techsil |
| XYRON™ X531V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| BRALEN® FB 08-65 | Slovnaft Petrochemicals, s.r.o. | LDPE | BRALEN® |
| Generic PC+TPU | Generic | PC+TPU | Generic |