TAROLOY 110
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xGxhN3_TAROLOY-110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PC/PET alloy, high impact strength dimensional stability. Good chemical and weather resistance. Available: all colors, UV stabilized (L), heat stabilised (H), release agent (W). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/1.2 kg) | 12 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.60 to 1.0 | % | |
| Across Flow | 0.60 to 1.0 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.080 | % | ASTM D570, ISO 62 |
| Saturation | 0.35 | % | ASTM D570 |
| Saturation, 23°C | 0.35 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 65.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 40 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2150 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 90.0 | MPa | ISO 178 |
| Yield | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 700 | J/m | ASTM D256, ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 120 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 130 | °C | ISO 306/B50, ASTM D1525 1 |
| CLTE - Flow (-30 to 30°C) | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 110 | °C | |
| Pre-heater | 110 to 120 | °C | |
| Drying Time | |||
| -- | 2.0 | hr | |
| Pre-heater | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GS40-66 22L-N | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Adell PP RR-39 | Adell Plastics, Inc. | PP Copolymer | Adell PP |
| Cellophane™ 335LMSCi | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| ElectriPlast® EP-SS/PC/ABS | Integral Technologies, Inc. | PC+ABS | ElectriPlast® |
| PAXOTHENE® NA207-66 | USI Corporation | LDPE | PAXOTHENE® |