Lighter™ S93
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Equipolymers |
| Trademark: | Lighter™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xGGXW1_Lighter-S93.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LIGHTER™ S93 is a polyester polymer modified to improve infrared reheating of preforms. LIGHTER S93 provides very good mechanical properties and a wide processing range on all injection molding machines. Moreover, preforms manufactured from LIGHTER S93 provide enhanced infrared heating rates, thus improving the operation of the stretch blow molding process, either increasing the maximum output or reducing the reheat energy. LIGHTER S93 is suitable for the production of bottles for both mineral water and carbonated soft drinks. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Density | 0.88 | g/cm³ | Internal Method |
| Moisture Content | < 0 | ppm | Internal Method |
| Acetaldehyde | < 1.0 | ppm | Internal Method |
| Crystallinity | > 50 | % | Internal Method |
| Intrinsic Viscosity | 0.78 to 0.82 | dl/g | Internal Method |
| Weight - 100 Granules | 1.5 | g | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color Coordinate - b | < 1.50 | Internal Method | |
| Fine Particles | < 500 | ppm | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 55.0 | MPa | |
| Break | 24.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.0 | % | |
| Break | 250 | % | |
| Flexural Modulus | 2100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 4.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 78.0 | °C | Internal Method |
| Vicat Softening Temperature | 77.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 247 | °C | Internal Method |
| CLTE - Flow | 8.3E-5 | cm/cm/°C | ISO 11359-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRISTAR® PC-10R-CL(22) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| Vydyne® R543H Black | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| ESTASTIR HG 0808 | Cossa Polimeri S.r.l. | PS (HIPS) | ESTASTIR |
| 3M™ Dyneon™ Fluoroelastomer FC 2176Z | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| Edgetek™ PC-15CF-15GF/000 NH FR V0 Black | PolyOne Corporation | PC | Edgetek™ |