Braskem PE EF2126S3
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xFg7GR_Braskem-PE-EF2126S3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EF2126S3 is a Low Density Polyethylene produced under high pressure conditions in an autoclave reactor. It offers excellent processability and optical properties. Additives: This resin contains slip and antiblock additives Application: This resin is recommended for use in extrusion of films for general purposes, technical films for automatic packaging and blends with LLDPE. Process: Blow Film Extrusion. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.921 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.6 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm | 160 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm | 200 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 38 µm | 25.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 20.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm | 290 | % | ASTM D882 |
| TD : Fracture, 38 µm | 1000 | % | ASTM D882 |
| Dart Drop Impact 1(38 µm) | 90 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 420 | g | ASTM D1922 |
| TD : 38 µm | 110 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 38.0 µm) | 100 | ASTM D2457 | |
| Haze | 7.0 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Recommended Blow Film Extrusion Conditions:Temperature Profile: 150°C to 165°CMass Temperature: 160°C to 165°CBlow up Ratio: 2.0 to 4.0 : 1Die Gap: 1.0 mmMinimum thickness:30 microns |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PC SC1005L | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| Braskem PP TI6800WV | Braskem America Inc. | PP Impact Copolymer | Braskem PP |
| DynaPath™ C2030CF | Polymer Dynamix | Nylon 66 | DynaPath™ |
| Elvaloy® AC 3217 | DuPont Packaging & Industrial Polymers | EnBA | Elvaloy® |
| Durethan® BM 430 H2.0 901510 | LANXESS GmbH | Nylon 6 | Durethan® |