PC/ABS, Maximum Toughness, Low Temperature Impact Strength, Elevated HDT |
General Information | |
---|---|
Features |
|
RoHS Compliance |
|
UL File Number |
|
Forms |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 1.14 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
230°C/3.8 kg | 2.4 | g/10 min | |
260°C/2.16 kg | 6.0 | g/10 min | |
260°C/3.8 kg | 20 | g/10 min | |
Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.70 | % | ISO 294-4 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Stress (Break) | 57.0 | MPa | ISO 527-2 |
Tensile Strain (Break) | 70 | % | ISO 527-2 |
Flexural Modulus | 2340 | MPa | ISO 178 |
Flexural Stress | 76.0 | MPa | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact Strength | ISO 180 | ||
-- | 50 | kJ/m² | |
-40°C | 20 | kJ/m² | |
-20°C | 35 | kJ/m² |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Heat Deflection Temperature (1.8 MPa, Unannealed) | 113 | °C | ISO 75-2/A |
Flammability | Nominal Value | Test Method | |
---|---|---|---|
Flame Rating (1.50 mm) | HB | UL 94 |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Retpol® 1236 | PolyPacific Pty. Ltd. | PP Homopolymer | Retpol® |
SCHULAFORM® 9 A | A. Schulman Europe | Acetal (POM) Copolymer | SCHULAFORM® |
Hanwha Total PP BJ352 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
Polifor® QD 813 Y001 NATURALE | SO.F.TER. SPA | PP Copolymer | Polifor® |
StarClear® 1025-0000 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarClear® |