Bayblend® FR3010 HF
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Bayblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xEIsIG_Bayblend-FR3010-HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Previous name Bayblend FR2010; (PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; easy-flow grade; Vicat/B 120 temperature = 108 °C; UL recognition 94 V-0 (1.5 mm); glow wire test (GWFI): 960 °C (2.0 mm); optimized processability; good light stability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (240°C/5.0 kg) | 25.0 | cm³/10min | ISO 1133 |
| Spiral Flow | 40.0 | cm | Internal Method |
| Molding Shrinkage 1 | ISO 2577 | ||
| Across Flow : 240°C, 3.00 mm | 0.50 to 0.70 | % | |
| Flow : 240°C, 3.00 mm | 0.50 to 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.50 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2700 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 60.0 | MPa | |
| Break, 23°C | 50.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 4.0 | % | |
| Break, 23°C | > 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 35 | kJ/m² | |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 106 | °C | ISO 306/B50 |
| -- | 108 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 7.6E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.20 | ||
| 23°C, 1 MHz | 3.10 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 4.0E-3 | ||
| 23°C, 1 MHz | 7.0E-3 | ||
| Comparative Tracking Index (Solution A) | 350 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.20 mm | 5VB | ||
| 3.00 mm | 5VA |
| Note Message | |
|---|---|
| 1 . | 150x105x3 mm, 80°C MT |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene P254-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Sylvin 6034-85 Grey 9561 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Braskem PP TI6550WV | Braskem America Inc. | PP Impact Copolymer | Braskem PP |
| ESENTTIA 25C35-EC | Polipropileno del Caribe S.A. | PP Impact Copolymer | ESENTTIA |
| Hostacom PPU X9067HS 4PK SOUL | LyondellBasell Industries | PP, Unspecified | Hostacom |