Delrin® FG500P NC010
| Category: | Acetal (POM) Homopolymer , ACETAL RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Delrin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xDGm27_Delrin-FG500P-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium Viscosity Acetal Homopolymer Developed for Food Contact Applications |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.9 | % | |
| Flow | 2.0 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 1.4 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | ||
| M-Scale | 92 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 17 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 30 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2800 | MPa | |
| 1000 hr | 1600 | MPa | |
| Flexural Modulus | 2900 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 8.0 | kJ/m² | |
| -30°C | 8.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 240 | kJ/m² | |
| 23°C | 300 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 158 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 94.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 155 | °C | ISO 306/B50 |
| Melting Temperature 1 | 178 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.1E-4 | cm/cm/°C | |
| Transverse | 1.1E-4 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.800 mm | HB | ||
| 1.50 mm | HB |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4905 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Sumitomo DAP FS-10 VO-P | Sumitomo Bakelite North America, Inc. | DAP | Sumitomo DAP |
| Next PMMA AX-01D.GY. | Next Polymers Ltd. | Acrylic (PMMA) | Next PMMA |
| Altuglas® MI-7T | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| NORYL™ SA120 resin | SABIC Innovative Plastics | PPE | NORYL™ |