TECACOMP® PPS TRM XS black 4009
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xD8F22_TECACOMPPPSTRMXSblack4009.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | |
| Apparent Density | 0.55 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (316°C/2.16 kg) | 35 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (316°C/2.16 kg) | 29.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.64 | % | ISO 294-4 |
| Flow | 0.13 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | < 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 22500 | MPa | ISO 527-2/50 |
| Tensile Stress | 135 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 0.50 | % | ISO 527-2/50 |
| Compressive Modulus | 4650 | MPa | ISO 604/1 |
| Compressive Stress | 155 | MPa | ISO 604/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 18 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 285 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 280 | °C | ISO 75-2/A |
| Glass Transition Temperature | 90.0 | °C | DIN 53765 |
| Melting Temperature | 280 | °C | DIN 53765 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 80°C | 9.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 4.7E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | DIN EN 821 | ||
| -- 1 | 0.70 | W/m/K | DIN EN 821 |
| -- 2 | 1.1 | W/m/K | DIN EN 821 |
| Service Temperature | |||
| long term | 230 | °C | |
| short term | 260 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 6.2E+3 | ohms·cm | ISO 3915 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | V-0 | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 - 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Processing (Melt) Temp | 300 - 350 | °C | |
| Mold Temperature | 140 - 160 | °C |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| 2 . | In-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon G2513H-01 | RheTech, Inc. | Nylon 66 | Rhelon |
| Exelene® PP R0200 | Montachem International, Inc. | PP Random Copolymer | Exelene® PP |
| DOW™ Electrical & Telecommunications HFDB-4201 SC K | The Dow Chemical Company | XLPE | DOW™ Electrical & Telecommunications |
| INLUBE PA66SI2IM | Infinity LTL Engineered Compounds | Nylon 66 | INLUBE |
| POLYFLON™ F-207 | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |