RapidCast™ RC-510
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | RapidCast™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xCyvMC_RapidCast-RC-510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| RC-510 is a rigid polyurethane formulated for room temperature meter-mix dispensing systems and short mold cycle times. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.08 | g/cm³ | |
| Cured | 1.12 | g/cm³ | |
| Base Resin | 1.20 | g/cm³ | |
| Molding Shrinkage - Flow | 0.20 to 0.60 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1860 | MPa | ASTM D790 |
| Flexural Strength | 87.6 | MPa | ASTM D790 |
| Compressive Modulus | 4000 | MPa | ASTM D695 |
| Compressive Strength | 63.4 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 21 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 157 | °C | |
| 1.8 MPa, Unannealed | 135 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 90 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 20 to 30 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.10 | Pa·s | |
| 25°C 2 | 0.70 | Pa·s | |
| 25°C 3 | 2.0 | Pa·s | |
| Curing Time (25°C) | 24 | hr | |
| Gel Time | 0.67 to 1.0 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 80 to 90 | ASTM D2240 | |
| Tensile Strength | 62.1 | MPa | ASTM D638 |
| Tensile Elongation at Break | 5.0 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® Marine-Tec lite | Röchling Engineering Plastics SE & Co. KG | TP, Unspecified | POLYSTONE® |
| Nypol® PA B3 HL VRM0310 NT361 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Hifax BC 72 A/1 | LyondellBasell Industries | PP Copolymer | Hifax |
| Polidan® T/A-LX | Solvay Specialty Polymers | XLPE | Polidan® |
| Starflam POK 25V Z27 - BK84034 | Eurostar Engineering Plastics | PK-Aliphatic | Starflam |