Network Polymers LDPE 10 0105
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Network Polymers LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xCwOiX_Network-Polymers-LDPE-10-0105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Network Polymers LDPE 10 0105 is an Ethylene Vinyl Acetate Copolymer (EVA) product. It is available in North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) 1(190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 4.6 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD | 146 | MPa | |
| 1% Secant, TD | 169 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break | 25.9 | MPa | |
| TD : Break | 24.7 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 180 | % | |
| TD : Break | 580 | % | |
| Dart Drop Impact | 190 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 200 | g | |
| TD | 90 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 88.9 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 71 | ASTM D2457 | |
| Haze | 6.4 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 218 MZ15 V25 BLACK 31 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Soarnol® TF2905B | Soarus L.L.C. | EVOH | Soarnol® |
| Grilon® BGZ-40 | EMS-GRIVORY | Nylon 6 | Grilon® |
| PENTAMID AB MC30 H RC schwarz | PENTAC Polymer GmbH | Nylon 66/6 | PENTAMID AB |
| Sylvin 8200-70 Brown 7390 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |