HAIPLEN H10 T6
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xClyRh_HAIPLEN-H10-T6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer 30% talcum filled, low flow, high stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 1.1 | % | Internal method |
| Flow direction | 1.1 | % | Internal method |
| Granule Humidity 1 | 0.050 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 2(550°C) | 30 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 30.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 30 | % | ISO 527-2/50 |
| Flexural Modulus 3 | 2500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 35 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ISO 306/A50 |
| -- | 95.0 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 4(2.00 mm) | < 100 | mm/min | ISO 3795 |
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Oxygen Index | 21 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 - 220 | °C | |
| Mold Temperature | 50.0 - 70.0 | °C | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| Pre-heat Temperature: 70 to 80°CPre-heat Time: 1 hr |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1 hr |
| 3 . | 1.0 mm/min |
| 4 . | US FMVSS302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sevrene® 4000-65A | Vi-Chem Corporation | PVC, Unspecified | Sevrene® |
| Cheng Yu PE221 | Cheng Yu Plastic Company Limited | LDPE | Cheng Yu |
| Fiberfil® J-60/30/E/HF | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| ESENTTIA 07R87DB | Polipropileno del Caribe S.A. | PP Random Copolymer | ESENTTIA |
| Karina IVORY PVC COMPOUND 750-35/1-B-AC-AS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |