Ebalta MG 454 / Comp. A+B
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xCGTcG_Ebalta-MG-454-Comp-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ebalta MG 454 is processed on a two-component low pressure device. After grinding with a sand paper , grit 280, the surface can be varnished with a commercial lacquer. For better adhesion we recommend the use of a primer coat. Applications
Properties
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 75 to 79 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2000 to 2200 | MPa | ISO 178 |
| Flexural Stress | 54.0 to 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 9.0 to 13 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 90.0 to 100 | °C | ISO 75-2/B |
| Glass Transition Temperature | 107 | °C | DSC |
| CLTE - Flow | 9.5E-5 | cm/cm/°C | DIN 53752 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 57 Mix Ratio by Weight: 60 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Post Cure Time | |||
| 80°C | 4.0 | hr | |
| 120°C | 2.0 | hr |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.00 | g/cm³ | |
| Curing Time (50°C) | 0.083 to 0.25 | hr | |
| Pot Life (20°C) | 1.0 to 1.3 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUZEX® 7300 | SK Global Chemical | HDPE | YUZEX® |
| Network Polymers PP PPH 30 2000 TF40 | Network Polymers, Inc. | PP Homopolymer | Network Polymers PP |
| Durethan® BKV 315 Z H2.0 901510 | LANXESS Asia/Pacific | Nylon 6 | Durethan® |
| LUVOCOM® 1-7360/EG | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Plasmer 1035NM/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |