XT polymer X800RG compound is an impact-modified acrylic-based multipolymer for molding and extrusion applications.

Typical properties of XT® polymer acrylic-based multipolymer compounds are:

outstanding thermoformability

superior heat distortion temperatures

excellent bonding and welding capabilities

good impact strength

good light transmission

resistant to EtO, gamma and E-beam sterilization

resistant to PVC stabilizers

The special properties of XT polymer X800RG compound are:

high melt flow rate

good chemical resistance

Application:
Used for food packaging and appliance parts.

General Information
Additive	Impact Modifier
Features	Bondability E-beam Sterilizable Ethylene Oxide Sterilizable Food Contact Acceptable Good Chemical Resistance Good Impact Resistance High Clarity High Flow High Heat Resistance Impact Modified Radiation Sterilizable Weldable
Uses	Appliance Components Battery Cases Food Packaging Household Goods Sporting Goods
Agency Ratings	EC 1907/2006 (REACH) FDA 21 CFR 176.170 USP Class VI
Appearance	Clear/Transparent Colors Available
Forms	Pellets
Processing Method	Extrusion Injection Molding Thermoforming

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.11	g/cm³	ASTM D792
Apparent Density	0.65	g/cm³	ASTM D1895
Melt Mass-Flow Rate (MFR) (230°C/5.0 kg)	11	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.40 to 0.70	%	ASTM D955
Water Absorption (Equilibrium)	< 0.30	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	22		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2960	MPa	ASTM D638
Tensile Strength	43.4	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	4.0	%
Break	6.0	%
Flexural Modulus	2210	MPa	ASTM D790
Flexural Strength	66.9	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
0°C, 6.35 mm	64	J/m
23°C, 6.35 mm	100	J/m

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm)	85.6	°C	ASTM D648
Vicat Softening Temperature	93.9	°C	ASTM D1525
CLTE - Flow (0 to 100°C)	8.6E-5	cm/cm/°C	ASTM D696

Optical	Nominal Value	Unit	Test Method
Transmittance (3200 µm)	86.0	%	ASTM D1003
Haze (3200 µm)	5.0	%	ASTM D1003
Yellowness Index (3.20 mm)	-1.0	YI	Internal Method

Resin Grade	Manufacturer	Category	Trademark
Prime Polypro™ J704UG	Prime Polymer Co., Ltd.	PP Copolymer	Prime Polypro™
ASI POLYETHYLENE LP 551-01	A. Schulman Inc.	HDPE Copolymer	ASI POLYETHYLENE
EXCELLOY CK10P	Techno Polymer Co, Ltd.	PC+ABS	EXCELLOY
Generic TPSiV	Generic	TPSiV	Generic
VALOX™ 815 resin	SABIC Innovative Plastics	PBT	VALOX™