Latene® 7 TR-V2
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xBMIm0_Latene-7-TR-V2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polypropylene homopolymer (PPh). Mineral filler. UL94 V-2 classified, halogens free. Product UL certified. Good surface appearance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.970 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.4 to 1.7 | % | |
| Flow : 2.00 mm | 1.4 to 1.7 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 2200 | MPa | |
| 60°C | 950 | MPa | |
| 90°C | 550 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 30.0 | MPa | |
| Yield, 60°C | 20.0 | MPa | |
| Yield, 90°C | 10.0 | MPa | |
| Break, 23°C | 25.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 6.0 | % | |
| Yield, 60°C | 8.0 | % | |
| Yield, 90°C | 9.0 | % | |
| Break, 23°C | 25 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 0.30 | kJ/m² | |
| 23°C | 1.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 15 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 45 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 90.0 | °C | |
| Vicat Softening Temperature | 100 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 4.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Oxygen Index | 29 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 to 220 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOREX TA 2111 HD | SILON s.ro | TP, Unspecified | TABOREX |
| Delrin® 100KM NC000 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| INNOPOL® PP CS 2-3302 TO BU | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |
| LUVOCOM® 50-7814/EM | Lehmann & Voss & Co. | PC | LUVOCOM® |
| LNP™ VERTON™ MV00ASU compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |