LNP™ LUBRICOMP™ KL004 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xBGKwa_LNPLUBRICOMPKL004compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KL004 is a compound based on Acetal Copolymer containing PTFE. Added features include Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound KL-4040 Product reorder name: KL004 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/5.0 kg) | 18.0 - 21.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 24 hours | 2.0 - 2.5 | % | ISO 294-4 |
| Flow direction : 24 hours | 2.0 - 2.5 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.26 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 47.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 10 | % | ISO 527-2/5 |
| Fracture | 23 | % | ISO 527-2/5 |
| Flexural Modulus 1 | ISO 178 | ||
| -- | 1800 | MPa | ISO 178 |
| 60°C | 1100 | MPa | ISO 178 |
| 100°C | 600 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 58.0 | MPa | ISO 178 |
| 60°C | 34.0 | MPa | ISO 178 |
| 100°C | 18.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.29 | ASTM D3702 Modified | |
| With Self-Static | 0.15 | ASTM D3702 Modified | |
| Flexural Strain at Break 2 | ISO 178 | ||
| -- | 7.0 | % | ISO 178 |
| 60°C | 7.0 | % | ISO 178 |
| 100°C | 7.0 | % | ISO 178 |
| Wear Factor - Washer | 10.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 64.0 mm Span) | 98.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 199 - 216 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYLEM® 66 GFR 30 FR V0 | EMAS Plastik San.Tic.AS. | Nylon 66 | NYLEM® |
| GPPC PS-302 | GPPC Chemical Co., Ltd. | PS (HIPS) | GPPC |
| Karina IVORY PVC COMPOUND -E CAK 65 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Jackdaw PLA HW18NT6651 | Jackdaw Polymers | PLA | Jackdaw PLA |
| LNP™ LUBRICOMP™ HFG25Z compound | SABIC Innovative Plastics | Nylon 11 | LNP™ LUBRICOMP™ |