LNP™ THERMOCOMP™ DF004 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xBEZ6G_LNPTHERMOCOMPDF004compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DF004 is a compound based on Polycarbonate resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound DF-1004 Product reorder name: DF004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.20 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.50 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.45 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.20 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5520 | MPa | ASTM D638 |
| -- | 5940 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 91.7 | MPa | ASTM D638 |
| Fracture | 102 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 9.5 | % | ASTM D638 |
| Fracture | 8.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5520 | MPa | ASTM D790 |
| -- | 6000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 149 | MPa | ASTM D790 |
| -- | 148 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 2 | 8.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 960 | J/m | ASTM D4812 |
| 23°C 3 | 59 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 144 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 139 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 141 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4MID® 9A22115 HR | 4Plas | Nylon 66 | 4MID® |
| Catalyst CT/1-LR | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| Delta ATR-2G40 | Delta Polymers | Acetal (POM) Copolymer | Delta |
| Durez® 33934 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| Hylon® N2200STHL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |