PPR PPHO02
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Premier Plastic Resins, Inc. |
| Trademark: | PPR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | x8N9TL_PPR-PPHO02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene Homopolymer 30% Glass Fiber Reinforced Black |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 72.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus - Tangent | 4480 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 146 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 135 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 38.0 - 71.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 210 - 238 | °C | |
| Middle Temperature | 210 - 238 | °C | |
| Front Temperature | 204 - 243 | °C | |
| Nozzle Temperature | 210 - 238 | °C | |
| Processing (Melt) Temp | 204 - 249 | °C | |
| Mold Temperature | 27.0 - 60.0 | °C | |
| Injection Pressure | 5.00 - 55.0 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 3.00 - 45.0 | MPa | |
| Back Pressure | 0.00 - 1.00 | MPa | |
| Cushion | 6.35 - 12.7 | mm |
| Injection instructions |
|---|
| Screw Speed: Slow-ModerateDecompression: 3.81 to 7.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Royalcast® 3109 | Chemtura | PUR-Ether | Royalcast® |
| TEREZ ABS/PC Blend 3000 | TER HELL PLASTIC GMBH | PC+ABS | TEREZ ABS/PC |
| Niche PCM18BK | Niche Polymer, LLC | PC | Niche |
| HiFill® PP 0202 B | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| Rotuba CAP CP800 (8% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |