Order Products : sales@su-jiao.com
HOPELEX AF-3200
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | HOPELEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | x7NgKW_HOPELEX-AF-3200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
20% glass-fiber reinforced PC/ABS, easy mold release Non-brominated, non-chlorinated flame retardant Optimum combination of high modulus and impact strength |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 93.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | > 4.0 | % | ASTM D638 |
| Flexural Modulus 3 | 5300 | MPa | ASTM D790 |
| Flexural Strength 4(Yield) | 137 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 120 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 280 to 300 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 260 to 280 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TF4THT (Series: FC/ht) | KRAIBURG TPE | TPE | THERMOLAST® K |
| U-polymer U-8400H | UNITIKA Plastics Division | Polyarylate | U-polymer |
| ALCOM® TPU 810/1998.1 CF | ALBIS PLASTIC GmbH | TPU, Unspecified | ALCOM® TPU |
| KOPELEN JM-355 | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
| Sylvin 2900-60 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |