CYCOLAC™ GRM2600L resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | x6MmuF_CYCOLAC-GRM2600L-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High Impact , good chemical resistance sheet grade ABS designed for refrigerator liner applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 2.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.45 to 0.65 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2410 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 41.4 | MPa | |
| Break | 35.9 | MPa | |
| Tensile Elongation 3(Break) | 55 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2310 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 400 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 46.9 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 100 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 85.6 | °C | |
| Vicat Softening Temperature | 113 | °C | ASTM D1525 6 |
| CLTE - Transverse (-40 to 40°C) | 7.2E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 to 93.3 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Suggested Shot Size | 50 to 70 | % | |
| Rear Temperature | 193 to 210 | °C | |
| Middle Temperature | 210 to 227 | °C | |
| Front Temperature | 232 to 254 | °C | |
| Nozzle Temperature | 232 to 274 | °C | |
| Processing (Melt) Temp | 232 to 274 | °C | |
| Mold Temperature | 48.9 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Rite® S-1180 | Lubrizol Advanced Materials, Inc. | Acrylic, Unspecified | Stat-Rite® |
| Vital-Line SHE8595 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| Nymax™ GF1200 A43 NATURAL | PolyOne Corporation | Nylon 66 | Nymax™ |
| Cri-Line HFLT-720 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Hanwha Total PP FH82 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |