Alkatuff® LL820
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Qenos Pty Ltd |
| Trademark: | Alkatuff® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | x5gN8m_Alkatuff-LL820.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LL820 is a hexene copolymer linear low density polyethylene, designed for general purpose injection molding. Application: LL820 is intended for general purpose injection molding, such as housware and lids. Specifications: If this product is used for food contact applications, then the user needs to ensure compliance with the requirements of AS2070-1999 and relevant FDA regulations. When used in accordance with FDA application guidelines, this product meets the requirements of FDA 21 CFR 177.1520 (c) 3.1a and AS2070-1999 section 4.1.1(a). This product should not be used in applications for holding food during cooking without the required compliance testing. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (100% Antarox CO-630, F50) | 700 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 46 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 13.0 | MPa | |
| Break | 10.0 | MPa | |
| Tensile Elongation 2(Break) | 500 | % | ASTM D638 |
| Flexural Modulus | 460 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Energy 3 | 9.60 | J | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (-40°C) | 90 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 60.0 | °C | |
| 1.8 MPa, Unannealed | 39.0 | °C | |
| Vicat Softening Temperature | 99.0 | °C | ASTM D1525 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYLOY® MG-2012N-V0 | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |
| CERTENE™ PHI-18 | Muehlstein | PP Homopolymer | CERTENE™ |
| OmniLon™ PA6/6 U GR33 HSL BK1000 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| Petrothene® NA362005 | LyondellBasell Industries | LDPE | Petrothene® |
| LEXAN™ EXL9112 resin | SABIC Innovative Plastics | PC | LEXAN™ |