Generic EVOH
| Category: | EVOH , Ethylene Vinyl Alcohol |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | x3zLXF_Generic-EVOH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic EVOH This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.13 - 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 210°C/2.16 kg | 3.0 - 12 | g/10 min | ASTM D1238 |
| 210°C/2.16 kg | 3.1 - 13 | g/10 min | ISO 1133 |
| Ethylene Content | 26.7 - 44.6 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 70 - 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2300 - 3020 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 24.3 - 68.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 11 - 17 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4750 - 4800 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability (23°C) | 0.387 - 1.52 | cm³/m²/24 hr | ASTM D1434 |
| Oxygen Permeability (23°C) | 1.0E-3 - 0.067 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (23°C) | 0.78 - 1.6 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | |||
| -- | 40.0 - 69.0 | °C | ISO 11357-2 |
| -- | 54.7 - 62.0 | °C | DSC |
| Vicat Softening Temperature | 145 - 179 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 164 - 189 | °C | |
| -- | 160 - 192 | °C | ISO 11357-3 |
| Peak Crystallization Temperature | |||
| -- | 141 - 164 | °C | ISO 11357-3 |
| -- | 144 - 164 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 170 - 180 | °C | |
| Cylinder Zone 2 Temp. | 190 - 200 | °C | |
| Cylinder Zone 3 Temp. | 210 - 220 | °C | |
| Cylinder Zone 4 Temp. | 220 - 231 | °C | |
| Cylinder Zone 5 Temp. | 220 - 231 | °C | |
| Adapter Temperature | 220 - 231 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic EVOHThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PS-GP1 | Polymer Resources Ltd. | PS (HIPS) | PRL |
| Alcryn® 2165 TR | Advanced Polymer Alloys | MPR | Alcryn® |
| DOW™ Electrical & Telecommunications DGDL-3479 NT | The Dow Chemical Company | HDPE | DOW™ Electrical & Telecommunications |
| Karina BLACK PVC COMPOUND -E 75850D48/ 1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1105-8205 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |