SABIC® PPcompound G3240A
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | x3gY46_SABIC-PPcompound-G3240A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound G3240A is a 40% short glass fiber reinforced Polypropylene for unter-the-hood and structural applications. The base material is a PP homopolymer and is available in standard black. The glass fibres are chemically coupled to the PP matrix SABIC® PPcompound G3240A is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.60 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm, Injection Molded) | 8900 | MPa | ISO 527-2/1A/5 |
| Tensile Stress (Break, 4.00 mm, Injection Molded) | 111 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break, 4.00 mm, Injection Molded) | 2.9 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1(Injection Molded) | 8900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C, Injection Molded) | 46 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C, Injection Molded) | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 161 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 153 | °C | ISO 75-2/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 4.1E-5 | cm/cm/°C | |
| 23 to 80°C | 4.3E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN T-035 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Fainplast PVC KL 92/1 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Hipolyene 8501 T6 B | Zylog Plastalloys | TPO (POE) | Hipolyene |
| InnoPlus HD6376EB | PTT Global Chemical Public Company Limited | HDPE | InnoPlus |
| Karina CLEAR PVC COMPOUND 85/200 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |