Braskem PE SLL118
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | x0GFo1_Braskem-PE-SLL118.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SLL118 is a Linear Low Density Polyethylene, copolymer of butene-1. Developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. It contains antioxidant additives. The minimum biobased content of this grade is 87%, determined according to ASTM D6866. Applications: Stretch films; liners; LDPE and HDPE blends and packages for general use. Others applications: blends for irrigation pipes. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.916 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 38 µm, Blown Film | 50.0 | MPa | |
| TD : Break, 38 µm, Blown Film | 40.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm, Blown Film | 1100 | % | |
| TD : Break, 38 µm, Blown Film | 1400 | % | |
| Flexural Modulus | ASTM D882 | ||
| 1% Secant, MD : 38 µm, Blown Film | 180 | MPa | |
| 1% Secant, TD : 38 µm, Blown Film | 200 | MPa | |
| Dart Drop Impact 1(38 µm, Blown Film) | 120 | g | ASTM D1709 |
| Elmendorf Tear Strength - TD (38 µm, Blown Film) | 370 | g | ASTM D1922 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 87 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYNIL® P36/4 | Nilit Plastics | Nylon 66 | POLYNIL® |
| Colorite 88 Series 6088 | Colorite Polymers | PVC, Unspecified | Colorite 88 Series |
| GERMADUR GF VO 30 | Kunststoff-Kontor-Hamburg GmbH | PBT | GERMADUR |
| Kuraray Poval® LM-10HD | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |
| Infino HM-4300G | LOTTE ADVANCED MATERIALS CO., LTD. | PPA | Infino |