LUBEXAN 2025 GREY TQ
| Category: | PC , Polycarbonate |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBEXAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wzIfaN_LUBEXAN-2025-GREY-TQ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on Polycarbonate. Second choice. Coloured. High MFR. For standard injection moulding. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 to 1.21 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 to 25 | g/10 min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.20 mm | 0.15 | % | |
| Saturation, 23°C, 3.20 mm | 0.36 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 to 2500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield | 45.0 to 50.0 | MPa | |
| Break | 40.0 to 45.0 | MPa | |
| Tensile Strain | ISO 527-2/1A/50 | ||
| Yield | 4.0 to 7.0 | % | |
| Break | 15 to 20 | % | |
| Flexural Modulus 1 | 1800 to 2200 | MPa | ISO 178 |
| Flexural Stress 2 | 50.0 to 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 to 25 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 400 to 450 | J/m | ASTM D256A |
| 23°C 3 | No Break | ASTM D256 | |
| 23°C | 20 to 25 | kJ/m² | ISO 180/A |
| 23°C 4 | 40 to 45 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 130 to 140 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 135 to 145 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 120 to 130 | °C | ASTM D648 |
| Glass Transition Temperature | 140 to 150 | °C | Internal Method |
| Vicat Softening Temperature | |||
| -- | 140 to 150 | °C | ISO 306/A120 |
| -- | 135 to 145 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 850 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propilven F-502 | Propilven, S.A. | PP Homopolymer | Propilven |
| Sinvicomp SFW7000 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Hanwha Total PE 4220U | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LLDPE | Hanwha Total PE |
| Hylex® P1025FRMA | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| K-vinyl 105 Deg C Rating Insulation (85-Wet) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |