VALOX™ ENH4550 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wz8AzU_VALOXENH4550resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.53 | g/cm³ | ASTM D792 |
| -- | 1.52 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 27 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow 1 | 0.10 - 0.50 | % | Internal method |
| Flow : 3.20mm | 0.10 - 0.50 | % | Internal method |
| Transverse flow 2 | 0.60 - 1.2 | % | Internal method |
| Transverse flow : 3.20mm | 0.50 - 1.1 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.23 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 3 | 9900 | MPa | ASTM D638 |
| -- | 10400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 4 | 105 | MPa | ASTM D638 |
| Yield | 112 | MPa | ISO 527-2/5 |
| Fracture 5 | 105 | MPa | ASTM D638 |
| Fracture | 112 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 6 | 2.0 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2/5 |
| Fracture 7 | 2.0 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 8 | 9100 | MPa | ASTM D790 |
| -- 9 | 9400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 170 | MPa | ISO 178 |
| Yield, 50.0mm span 10 | 161 | MPa | ASTM D790 |
| Flexural Strain at Break 11 | 2.0 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C | 7.0 | kJ/m² | ISO 179/2C |
| 23°C 12 | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength | ISO 179/2U | ||
| -30°C | 33 | kJ/m² | ISO 179/2U |
| 23°C | 36 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| -30°C | 59 | J/m | ASTM D256 |
| 23°C | 62 | J/m | ASTM D256 |
| -30°C 13 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C 14 | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 470 | J/m | ASTM D4812 |
| 23°C | 520 | J/m | ASTM D4812 |
| -30°C 15 | 29 | kJ/m² | ISO 180/1U |
| 23°C 16 | 33 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 6.50 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 216 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 17 | 219 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 204 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 18 | 201 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 202 | °C | ASTM D1525 19 |
| -- | 215 | °C | ASTM D1525 20 |
| -- | 219 | °C | ISO 306/A50 |
| -- | 206 | °C | ISO 306/B50, ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 2.7E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 150°C | 2.2E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 80°C | 2.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.1E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 150°C | 7.7E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 7.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 9.1E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 140 | °C | UL 746 |
| RTI | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 - 1.0E+16 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | ASTM D149 | ||
| 3.20 mm, in Air | 21 | kV/mm | ASTM D149 |
| 3.20 mm, in Oil | 21 | kV/mm | ASTM D149 |
| Arc Resistance 21 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Comparative Tracking Index | 300 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | UL 94 | |
| 3.00 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index (0.750 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 775 | °C | IEC 60695-2-13 |
| 3.00 mm 22 | 775 | °C | IEC 60695-2-13 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (250°C, 1500 sec^-1) | 210 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 - 60.0 | °C | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Nozzle Temperature | 230 - 255 | °C | |
| Processing (Melt) Temp | 245 - 260 | °C | |
| Mold Temperature | 40.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Tensile Bar |
| 3 . | 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | Type 1, 5.0 mm/min |
| 7 . | Type 1, 5.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 2 mm/min |
| 12 . | 80*10*4 sp=62mm |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 mm |
| 18 . | 80*10*4 mm |
| 19 . | 标准 B (120°C/h), 载荷2 (50N) |
| 20 . | 速率 A (50°C/h), 载荷2 (50N) |
| 21 . | Tungsten electrode |
| 22 . | by VDE |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 9346 | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| TARFLON™ LC1700 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| VESTOLIT® E 7031 | VESTOLIT GmbH & Co. KG | PVC Homopolymer | VESTOLIT® |
| UNISOFT TPE™ ST-55A-BK-1-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| SD POLYCA™ IM6023 | Sumika Styron Polycarbonate Limited | PC+ABS | SD POLYCA™ |