SABIC® PP RELY 71EK71PS
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wz3UK1_SABIC-PP-RELY-71EK71PS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This block copolymer has a high molecular weight and is provided with a long-term heat stabilisation package. It exhibits high stiffness in combination with outstanding impact strength even at low temperatures. This material is used for extrusion of sewage pipe applications and can also be used for blow-moulding and sheet extrusion. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 | |
| Shore Hardness (Shore D) | 66 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1500 | MPa | ASTM D638 |
| -- | 1450 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 29.0 | MPa | ASTM D638 |
| Yield | 28.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 9.0 | % | ASTM D638 |
| Yield | 8.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 7.0 | kJ/m² | |
| 0°C | 20 | kJ/m² | |
| 23°C | 80 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -20°C | 70 | J/m | ASTM D256A |
| 0°C | 350 | J/m | ASTM D256A |
| 23°C | No Break | ASTM D256A, ISO 180/1A | |
| -20°C | 6.0 | kJ/m² | ISO 180/1A |
| 0°C | 35 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 100 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 95.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 55.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 156 | °C | ASTM D1525, ISO 306/A120 5 6 |
| -- | 81.0 | °C | ASTM D1525, ISO 306/B120 6 7 |
| Oxidation Induction Time (200°C) | > 100 | min | EN 728 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trovicel® 10 mm | Röchling Engineering Plastics SE & Co. KG | PVC, Flexible | Trovicel® |
| Ultrathene® UE624000 | LyondellBasell Industries | EVA | Ultrathene® |
| DIALAC® TW15B | UMG ABS, Ltd. | ASA | DIALAC® |
| HYBRAR™ 5125 | Kuraray Co., Ltd. | TPE | HYBRAR™ |
| OnForce™ LFT PP-50LGF/000 8001 | PolyOne Corporation | PP, Unspecified | OnForce™ LFT |