INSULCAST® 116 FR-FC-FS
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULCAST® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wynyF6_INSULCAST-116-FR-FC-FS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INSULCAST 116 FR-FC-FS is a one to one ratio (weight or volume) epoxy potting and casting compound designed for production use. The convenient mixing ratio makes it ideal for production line mixing as well as automatic dispensing. The INSULCAST 116 FR-FC-FS is among the safest epoxy compounds available. It appreciably reduces the risk of eye, skin or respiratory problems generally associated with the use of epoxy compounds. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 65.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Compressive Strength | 79.3 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 4.5E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.65 | W/m/K | |
| Heat Deflection Temperature | 80 | °C | |
| Service Temperature | 105 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tack Free Time 1 | 6.0 | hr |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 4.40 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.020 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Volume: 1.0 Mix Ratio by Weight: 1.0 | ||
| Part B | Mix Ratio by Volume: 1.0 Mix Ratio by Weight: 1.0 | ||
| Shelf Life (25°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 2 | Black | ||
| -- 3 | Grey | ||
| Density | |||
| -- 4 | 1.50 | g/cm³ | |
| -- 5 | 1.50 | g/cm³ | |
| Viscosity | |||
| -- 6 | 7.2 | Pa·s | ASTM D2393 |
| -- 7 | 9.8 | Pa·s | |
| -- 8 | 10 | Pa·s | ASTM D2393 |
| Curing Time (22°C) | 16 to 24 | hr | |
| Gel Time (25°C) | 60 | min | |
| Pot Life 9 | 30 | min |
| Note Message | |
|---|---|
| 1 . | 150 gram mass |
| 2 . | Part A |
| 3 . | Part B |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | Part A |
| 7 . | Mixed |
| 8 . | Part B |
| 9 . | 100 gram mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2000 B-390 | RTP Company | PSU Alloy | RTP |
| Axiall PVC 50897 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Elastron庐 G P.G101.A45.B | Elastron USA, Inc. | SEBS | Elastron® G |
| Elvaloy® AC 34035 | DuPont Packaging & Industrial Polymers | EBA | Elvaloy® |
| Rotuba CAP CP800 (16% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |